無縫鋼管數字代號及化學成分(熔煉分析)應符合表1的規定

　6.1牌號、代號及化學成分無縫鋼管數字代號及化學成分(熔煉分析)應符合表1的規定6.1.1.1鋼的硫、磷含量應符合表2的規定。6.1.1.2使用廢鋼冶煉的鋼允許含銅量不大于〇.3〇^L 6.1.1.3熱壓力加工用鋼的銅含量應不大于〇.2〇%。5.1. 1. 4鉛浴淬火(派登脫)鋼絲用的35?85銅的錳含量為0. 30%?0. 60%;鉻含量不大于0.10%, 鎳含量不大于〇. 15%,銅含量不大于0.20%;硫、磷含量應符合鋼絲標準要求。6.1.1_ 5 〇8鋼用鋁脫氧冶煉鎮靜鋼，錳含量下限為0. 25%,硅含量不大于0_ 03%，鋁含量為0. 02%?0.07%。此時鋼的牌號為08AU 表1 序號統一數字代號牌號化學成分，％ CSiMnCrNiCu 不大于 1U2008008F0.05 ?0.11<0, 030. 25?0. 500.100. 300. 25 2U2010010F0. 07 ?0.13<0?0?0. 25?0. 500.150.300. 25 3U2015015F0? J_2 ?0.18<0. 070. 25?0. 500* 250.300,25 4U20082080.05 ?0.110? 17 ?0? 370. 35 ?0. 650.100.300-25 5U20102100.0 卜 0,130? 17 ?0? 370. 35 ?0. 650.150. 300. 25 6U20152150,12 ?0.180? 17 ?0, 370* 35 ?0* 650. 250.300. 25 7U20202200,17 ?0.230? 17?0, 370. 35—0*650. 250. 300, 25 8U20252250.22 ?0.290? 17?0, 370. 50?0, 800.250.300* 25 9U20302300. 27?0. 340-17?0, 370. 50?0. S00. 250,300. 25 10U2035235CK 32?0. 390.17?0. 370- 50?0? 800. 250. 300. 25 11U2040240(X 37 ?0* 440.17 ?0.370, 50?0, 800. 250.300. 25 12U20452450. 42?0. 500.17 ?0*370, 50?0. 800. 250.300. 25 13U20502500■ 47 ?0? 55(>?17 ?0.370. 50?0. 800. 250.300. 25 14U20552550. 52?0. 600,17 ?0,370. 50?0. 800. 250. 300* 25 15U20602600. 57?0. 650,17 ?0*370. 50?0. 800. 250.300. 25 16U20652650, 62?0. 700.17 ?0.370, 50?0. 800,250,300,25 17U20702700, 67?0. 750*17 ?370. 50?0. 800. 250. 300. 25 18U20752750. 72?0. 800? 17?0. 370. 50?0. 800. 250. 300. 25 19U20802800, 77?0. 850.17 ?0.370. 50?0. 800. 250.300. 25 20U20852850, 82 ?a 900.17?0. 370, 50?0. 800. 250.300.25 21U2115215Mn0.12 ?0.180,17?0, 370, 70?1. 000,250,300.25 22U2120220Mn0,17—0. 230? 17?0. 370. 70?:L 000. 250, 300. 25 23U2125225Mn0_ 22?0. 290.17?0. 370. 70?1. 000. 250.300. 25 24U2130230Mn0? 27 ?0? 340.17?0. 370? 70?1. 000. 250.300.25 25U2135235Mn0, 32 ?0, 390? 17?0. 370, 70?1, 000. 250. 300,25 26U2140240Mn0. 37 ?0. 440」7?0*370, 70?1. 000. 250. 300.25 27U2145245Mn0. 42?0, 500.17 ?0.370? 70?1. 000.250. 300. 25 28U2150250Mn0. 48?0, 560.17 ?0? 370. 70?1. 000.250. 300. 25 29U2160260Mn0? 57 ?0? 65(X 17?0. 370. 70?1. 000* 250. 300* 25 30U2165265Mn0. 62?0. 700,17?0. 370? 90?1. 200.250.300. 25 31U2170270Mn0. 67?0. 750+17?0? 370, 90?1. 200,250. 300,25 注：表1所列牌號為優質鉬如果是高級優質鋼,在牌號后面加“A”(統一數字代號后一位數字改為“3”）;如 果是特級優質鋼，在牌號后面加°E” (統一數字代號后一位數字改為“6”）；對于沸騰鋼，牌號后面為“F” (統一數字代號后一位數字為“0”）f對于半鎮靜鋼，牌號后面為“b”(統一數字代號后一位數字為“1”）無縫鋼管